Brass Shell Cases Without Primers (Lake/Lace)
Brass Shell Cases Without Primers (Lake/Lace). Shall consist of clean fired 70/30 brass shell cases free of primers and any other foreign material.
Raw Material Information
Name | Full Name | Description |
---|---|---|
Clove | Clove No.1 COPPER WIRE NODULES |
It is composed of copper wire thicker than No. 16 B&S wire gauge (1.29mm of diameter) and cable scrap crushed. However, hardened wire or foreign substance should not be included, and plating, sheath, alloy wire, burnt wire and corroded wire should be excluded. Minimum copper content is 99%. |
Barley | Barley No.1 COPPER WIRE |
It is composed of copper wire thicker than No. 16 B&S wire gauge (1.29mm) and cable scrap. However, hardened wire or foreign substance should not be included Plating, sheath, alloy wire, burnt wire and corroded wire should be excluded. Compressed product is depending on the agreement between buyer and seller. |
Berry | Berry No. 1 COPPER WIRE |
It is composed of copper wire thinner than No. 16 B&S wire gauge (1.29mm) and cable scrap. However, hardened wire or foreign substance should not be included, and plating, sheath, alloy wire and excessively burnt wire should be excluded. Compressed product is depending on the agreement between buyer and seller. |
Cobra | Cobra No. 2 COPPER WIRE NODULES |
General name for copper wire chopping scrap and copper content should be higher than at least 98%. Contents of other impurities and sheath should be less than 1% each. |
Birch | Birch No. 2 COPPER WIRE |
It is composed of various copper wire scrap with at least 96% of copper content. Contents of other impurities and sheath should be less than 1% each. Compressed product is depending on the agreement between buyer and seller. |
Cliff | Cliff No. 2 COPPER |
It is composed of unalloyed scraps (pipe, plate and lump type) with at least 96% of copper content. However, connection area except lead, tin, soldering, brass wire, bronze wire, oil, iron, nonmetal and copper, insulated wire, wire as thin as hair shaft, wire burnt to be broken and ash should not be excessive. Compressed product is depending on the agreement between buyer and seller. |
Label | Label NEW BRASS CLIPPINGS |
It is composed of lead-free brass plate and cut and punched shape of lead-free brass plate. Plated and contaminated object, muntz metal and naval brass should be excluded, and the punch size smaller than 1/4 inch should be less than 10%. |
Lake | Lake BRASS SMALL ARMS AND REFLE SHELLS, CLEAN FIRED |
It is composed of empty cartridge for rifle with 70/30 brass fired, and warhead, detonator, iron and other external materials should be excluded. |
Lace | Lace BRASS SHELL CASES WITHOUT PRIMERS |
It is composed of large empty cartridge with 70/30 brass fired, and detonator, iron and other external materials should be excluded. |
Pallu | Pallu ALUMINUM BRASS CONDENSER TUBES |
Condenser tube means the pipe of heat exchanger, and it is the aluminum brass scrap with 2% of Al added to 8:2 brass. It means the pure scrap with good quality while objects alloyed with nickel and tin are excluded. |
Night | Night YELLOW BRASS ROD |
It is composed of chip shape created after cutting the brass billet with less than 0.75% of tin + iron. Aluminum, manganese, synthetic products, gun metal cutting chip, abrasive powder and high tin alloy should not be included, and iron, oil and water contents should not exceed 3%. |
Noble | Noble NEW YELLOW BRASS ROD ENDS |
It is composed of brass cutting billet, broken extruded product and broken forged product with less than 0.75% of tin + iron. Aluminum, manganese, synthetic products, gun metal and high tin alloy should not be included. |
Honey | Honey YELLOW BRASS SCRAP |
It is composed of brass casting products with plated brass included, rolled products, wire rods, pipes and other yellow brass. Manganese bronze, aluminum bronze, various radiators or radiator parts, iron and excessively dirty or corroded products should be excluded. |
Ebony | Ebony COMPOSITION OR RED BRASS |
It is a bronze scrap which is composed of the parts of valves, machineries, etc. It is mostly alloyed with copper, tin, zinc and lead, and it is graded on Cu and Sn contents. Other scraps, such as Si or Al alloyed scrap, various brass scrap, etc., should be excluded. |
Ocean | Ocean Mixed Unsweated Auto RADIATORS |
It is composed of radiators which excluded the aluminum radiators and the radiator mixed with iron. Iron weight of all radiators can be the weight reduction target from the weight calculation, and total weight of radiator should be included in the weight information unless stated separately. |